AMPLIFY™ IO 3801B

Category:	Ionomer , Functional Polymer
Manufacturer:	The Dow Chemical Company
Trademark:	AMPLIFY™ IO
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	YvSbeW_AMPLIFY-IO-3801B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
AMPLIFY™ IO 3801B Ethylene Acrylic Acid Ionomer is designed for blown and cast film coextrusion for flexible packaging applications. It provides excellent sealability in coextrusions with nylon and other film structures with low blocking. For Food and Specialty Applications Excellent sealant for use in blown and cast film coextrusions Complies with: U.S. FDA 21 CFR 177.1310(b) Consult the regulations for complete details.

General Information
Additive	Anti-caking agent (2000 ppm)
Agency Ratings	FDA 21 CFR 177.1310 (b)
Forms	Particle
Processing Method	Blow film Co-extrusion molding cast film

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.940	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	1.3	g/10 min	ASTM D1238
Ion Type	Sodium (Na)

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	51	µm
Tensile Strength ¹			ASTM D882
MD : Yield, 51 µm	15.2	MPa	ASTM D882
TD : Yield, 51 µm	12.5	MPa	ASTM D882
MD : Fracture, 51 µm	33.6	MPa	ASTM D882
TD : Fracture, 51 µm	34.3	MPa	ASTM D882
Tensile Elongation ²			ASTM D882
MD : Fracture, 51 µm	280	%	ASTM D882
TD : Fracture, 51 µm	400	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	95.0	°C	Internal method

Extrusion instructions
吹塑薄膜的制造条件：用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。螺杆尺寸：A 和 B = 2.5 英寸 (64 mm)；C = 2 英寸 (51 mm)；30:1 L/D/尺寸螺杆类型：A= HS；B = DSB II；C = SFSM 模具间隙：70 密尔 (1. 78 mm) 熔体温度：A 和 B = 420°F (216°C)，C = 470°F (243°C) 输出：模具周长的 10 磅/小时/英寸模具直径：8 英寸放大比：2.5:1 螺杆速度：45 rpm 冷冻线高度：30 分钟 (762 mm)

Extrusion instructions

吹塑薄膜的制造条件：用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。螺杆尺寸：A 和 B = 2.5 英寸 (64 mm)；C = 2 英寸 (51 mm)；30:1 L/D/尺寸螺杆类型：A= HS；B = DSB II；C = SFSM 模具间隙：70 密尔 (1. 78 mm) 熔体温度：A 和 B = 420°F (216°C)，C = 470°F (243°C) 输出：模具周长的 10 磅/小时/英寸模具直径：8 英寸放大比：2.5:1 螺杆速度：45 rpm 冷冻线高度：30 分钟 (762 mm)

Note Message
1 .	The monolayer film data showed no resistance to caking.
2 .	The monolayer film data showed no resistance to caking.

Resin Grade	Manufacturer	Category	Trademark
QR Resin QR-1235P	QTR, Inc.	PC Alloy	QR Resin
THERMOLAST® K TF8THT (Series: FC/ht)	KRAIBURG TPE	TPE	THERMOLAST® K
INSTRUC PPSLGF10	Infinity LTL Engineered Compounds	PPS	INSTRUC
Sylvin 3290-85 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Veradel® A-101	Solvay Specialty Polymers	PESU	Veradel®