ACLAR® UltRx 4000 film
| Category: | PCTFE , Polychlorotrifluoroethylene |
| Manufacturer: | Honeywell |
| Trademark: | ACLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YdMQrt_ACLAR-UltRx-4000-film.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aclar UltRx 4000 film is a 4.00 mil PCTFE homopolymer, high performance barrier film for the pharmaceutical and medical industries. It thermoforms well on conventional blister packaging equipment and provides the highest barrier of any clear film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.11 | g/cm³ | ASTM D1505 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| MD : 100 µm | 1240 | MPa | ASTM D882 |
| TD : 100 µm | 1240 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 100 µm | 51.7 | MPa | ASTM D882 |
| TD : Yield, 100 µm | 37.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 100 µm | 190 | % | ASTM D882 |
| TD : Yield, 100 µm | 200 | % | ASTM D882 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 100 µm, 40°C, 75% RH | 0.048 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 100 µm, 38°C, 100% RH | 4.2E-3 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 100 µm, 25°C, 60% RH | 9.3E-3 | g·mm/m²/atm/24 hr | ASTM F1249 |
| 100 µm, 30°C, 60% RH | 0.016 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 211 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (102 µm) | < 1.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Yield, No Standard: 4.67 m²/kgTensile Strength @ Yld, ASTM D882, MD, 4 mil: 6000 to 9000 psiTensile Strength @ Yld, ASTM D882, TD, 4 mil: 4000 to 7000 psiTensile Elongation @ Yield, ASTM D882, MD, 4 mil: 150 to 225%Tensile Elongation @ Yield, ASTM D882, TD, 4 mil: 175 to 225%Secant Modulus, ASTM D882, 4 mil, MD & TD: 160000 to 200000Crystalline Melting Point, ASTM D4591: 211 °CDimensional Stability, ASTM D1204, MD & TD: /= 42 dynes/cm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 1500K | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| DENKA POVAL K-17U6 | Denka Company Limited | PVOH | DENKA POVAL |
| ExxonMobil™ LLDPE LL 3402.48 Cast | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| INEOS HDPE K44-15-186 | INEOS Olefins & Polymers USA | HDPE Copolymer | INEOS HDPE |
| Delon 6055 | Shanghai Lin Gen Rubber Materials Co., Ltd. | TEEE | Delon |