Radiopaque compound based on Polypropylene homopolymer (PPh). Special mineral filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.5 to 1.9 | % | |
| Flow : 2.00 mm | 1.5 to 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 20.0 | MPa | |
| Break, 23°C | 15.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 4.5 | % | |
| Break, 23°C | > 100 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stat-Tech™ ST3200-0005 ES RS | PolyOne Corporation | PC | Stat-Tech™ |
| VITAMIDE® AS30BK8522 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| TRISTAR® PC-10R-(IM) | Polymer Technology and Services, LLC | PC | TRISTAR® |
| AKROMID® A3 1 FR natural (3028) | AKRO-PLASTIC GmbH | Nylon 66 | AKROMID® |
| LNP™ LUBRICOMP™ DBL349E compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |