LNP™ THERMOCOMP™ KF004AL compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | YIuZZ4_LNPTHERMOCOMPKF004ALcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP KF004AL is a compound based on Acetal Homopolymer resin containing Glass Fiber. Added features of this material include: Low Extractible. Also known as: LNP* THERMOCOMP* Compound KF-1004 D LE Product reorder name: KF004AL |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8620 | MPa | ASTM D638 |
| Tensile Strength (Break) | 60.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.7 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 420 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 149 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRAN® PA3230 | SAMBARK | Nylon, Unspecified | SUPRAN® |
| V-TEM 150 | S&E Polymer Solutions, Inc. | TPE | V-TEM |
| Deprene 101-87 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |
| Sylvin 2999-67LG Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® BC 30 S 000000 | LANXESS GmbH | Nylon 6 | Durethan® |