ALTECH® PS-HI A 1000/100
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALTECH® PS-HI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XmtRsl_ALTECH-PS-HI-A-1000-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALTECH® PS-HI A 1000/100 is a High Impact Polystyrene product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Applications of ALTECH® PS-HI A 1000/100 include medical/healthcare and electrical/electronic applications. Characteristics include:
|
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 12 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 87.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 | MPa | ISO 527-2 |
| Tensile Stress | 23.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 40 | % | ISO 527-2 |
| Flexural Modulus | 1900 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | 110 | kJ/m² | |
| -40°C | 85 | kJ/m² | |
| -20°C | 110 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| Circulation Dryer | 60.0 to 80.0 | °C | |
| Desiccant Dryer | 60.0 to 80.0 | °C | |
| Drying Time | |||
| Circulation Dryer | 2.0 to 3.0 | hr | |
| Desiccant Dryer | 2.0 to 3.0 | hr | |
| Processing (Melt) Temp | 180 to 260 | °C | |
| Mold Temperature | 10.0 to 70.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenopom® POM B3 HF AML0337 PR323 | Petropol Industry and Trade of Polymers LTDA | Acetal (POM) Copolymer | Tenopom® POM |
| Xuchuan XCW-8550C | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Karina IVORY PVC COMPOUND -E 70900-35/ 1-F-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® 3010-15 | LG Chem Ltd. | PC | Lupoy® |
| POLYCASA® ACRYL G 88 Q18 | Polycasa | Acrylic (PMMA) | POLYCASA® ACRYL |