NORYL™ NH7111E resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XmlXAm_NORYL-NH7111E-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL EXNL0280 is a glass fiber reinforced, injection moldable modified polyphenylene ether resin. Designed for good dimensional stability and low warpage, this resin also uses non-halogenated FR additives to achieve a V1 UL94 rating at 1.6 mm and V0 UL94 at 3.00mm with a CTI value of 400 V. NORYL EXNL0280 may be an excellent material candidate for application requiring electrically insulating properties, low moisture absorption, low warpage and thin wall flame resistance. Available in limited light grey colors |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 18 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.23 | % | |
| Equilibrium, 23°C, 50% RH | 0.070 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3600 | MPa | ASTM D638 |
| -- | 3790 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 69.0 | MPa | ASTM D638 |
| Yield | 76.0 | MPa | ISO 527-2/5 |
| Break 3 | 66.6 | MPa | ASTM D638 |
| Break | 75.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.2 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2/5 |
| Break 5 | 4.5 | % | ASTM D638 |
| Break | 3.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 3570 | MPa | ASTM D790 |
| -- 7 | 3620 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 127 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 26 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 45 | J/m | ASTM D256 |
| 23°C 10 | 7.0 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 10.6 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 140 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 140 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ASTM D1525 12 |
| -- | 155 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+13 to 5.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 14 to 16 | ohms·cm | IEC 60093 |
| Electric Strength (3.20 mm, in Oil) | 27 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 2.97 | IEC 60250 | |
| Comparative Tracking Index | 400 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 4 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 0 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm, Testing by SABIC | V-1 | ||
| 3.00 mm, Testing by SABIC | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 775 | °C | |
| 2.00 mm | 775 | °C | |
| 2.50 mm | 775 | °C | |
| 3.00 mm | 775 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2200 HF TFE 20 | RTP Company | PEEK | RTP |
| Silopren® Electro 242-0 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| Sup-tech A706SH | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon, Unspecified | Sup-tech |
| DOWLEX™ 2740G (Tape) | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Hypel® PELD20/.920 | Entec Polymers | LDPE | Hypel® |