Generic HDPE, HMW
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Xkb6tn_Generic-HDPE-HMW.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic HDPE, HMW This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.940 - 0.956 | g/cm³ | ASTM D792 |
| 23°C | 0.943 - 0.959 | g/cm³ | ISO 1183 |
| -- | 0.948 - 0.960 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 0.027 - 0.28 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 5.6 - 11 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (23°C) | 15.0 - 1010 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 61 - 65 | ASTM D2240 | |
| 23°C | 60 - 64 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 595 - 1320 | MPa | ASTM D638 |
| 23°C | 900 - 1200 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 22.5 - 30.2 | MPa | ASTM D638 |
| Yield, 23°C | 21.8 - 27.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 24.5 - 40.0 | MPa | ASTM D638 |
| Tensile Strain | |||
| Yield, 23°C | 9.0 - 10 | % | ISO 527-2 |
| Fracture, 23°C | 480 - 800 | % | ASTM D638 |
| Fracture, 23°C | 300 - 820 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 677 - 1530 | MPa | ASTM D790 |
| 23°C | 1040 - 1250 | MPa | ISO 178 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 13 - 21 | µm | |
| secant modulus | ASTM D882 | ||
| MD | 517 - 1240 | MPa | ASTM D882 |
| TD | 800 - 1300 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 29.6 - 41.0 | MPa | ASTM D882 |
| TD : Yield | 28.0 - 34.6 | MPa | ASTM D882 |
| MD : Fracture | 49.0 - 63.7 | MPa | ASTM D882 |
| TD : Fracture | 28.3 - 67.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture | 300 - 600 | % | ASTM D882 |
| TD : Fracture | 390 - 700 | % | ASTM D882 |
| Dart Drop Impact (23°C) | 6.0 - 380 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD | 0.60 - 15 | g | ASTM D1922 |
| TD | 9.2 - 87 | g | ASTM D1922 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 53 - 850 | J/m | ASTM D256 |
| Tensile Impact Strength (23°C) | 251 - 386 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 67.6 - 78.3 | °C | ASTM D648 |
| Brittleness Temperature | -118 - -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | |||
| -- | 124 - 130 | °C | ASTM D1525 |
| -- | 73.0 - 128 | °C | ISO 306 |
| Melting Temperature | 127 - 130 | °C | |
| CLTE - Flow | 1.2E-4 - 1.4E-4 | cm/cm/°C | ASTM D696 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 156 - 206 | °C | |
| Cylinder Zone 2 Temp. | 189 - 205 | °C | |
| Cylinder Zone 3 Temp. | 195 - 218 | °C | |
| Cylinder Zone 4 Temp. | 199 - 250 | °C | |
| Melt Temperature | 199 - 255 | °C | |
| Die Temperature | 200 - 254 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic HDPE, HMWThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M2101R (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Copolymer | Sanren |
| ACCUTECH™ HP0339T10L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Dryflex® 662750S | ELASTO | SEBS | Dryflex® |
| Hanwha Total PP HS120 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| SEQUEL® 1835-AX BLK | LyondellBasell Industries | PP, Unspecified | SEQUEL® |