Clearflex庐 RL 50 U
| Category: | LMDPE , Linear Medium Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WiuGdN_Clearflex-RL-50-U.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex RL 50 U is a linear medium density polyethylene resin, with antioxidants and UV stabilizers, suitable for rotomoulding applications. Items manufactured with Clearflex RL 50 U show good mechanical properties and high environmental stress crack resistance (ESCR). Main Application Thanks to good mechanical properties and high ESCR, Clearflex RL 50 U is recommended for the production of high capacity containers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.941 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (Injection Molded) | > 500 | hr | ISO 22088 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Injection Molded | 19.0 | MPa | |
| Break, Injection Molded | 20.0 | MPa | |
| Tensile Strain (Break, Injection Molded) | > 700 | % | ISO 527-2 |
| Flexural Modulus (Injection Molded) | 730 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Drop Impact Resistance (Rotomolded Specimen) | 200 | J/cm | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 118 | °C | ISO 306/A |
| Melting Temperature | 128 | °C | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 230 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® CP 2002 | Plastic Solutions, Inc. | PP Impact Copolymer | PrimaFlex® |
| Badamid® LA70 GF30 TM-Z2 | Bada AG | Nylon 66 | Badamid® |
| Fiberfil® J-60/30/E5 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| Paxon™ AA48-002 | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |
| Daelim Po1y® XP9200EN | DAELIM INDUSTRIAL CO., LTD. | mLLDPE | Daelim Po1y® |