INEOS Wire & Cable BPD3642
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | INEOS Olefins & Polymers Europe |
| Trademark: | INEOS Wire & Cable |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | WGHPI7_INEOS-Wire-Cable-BPD3642.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Applications BPD3642 is a LLDPE copolymer containing hexene-1 as comonomer which, when compounded with suitable additives, is designed for silane crosslinked LV insulation. BPD3642 can be used in a silane one step crosslinking process (Monosil® for example) and in a silane two step crosslinking process (Sioplas® process). BPD3642 has been developed specifically to provide enhanced crosslinking and extrusion performances, thanks to proprietary process and catalyst and fit for purpose product design.
Applications BPD3642 is a LLDPE which, when compounded with suitable additives, is designed for jacketing of cables, especially power cables. BPD3642 combines an enhanced environmental stress cracking resistance to excellent mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance (10% Igepal, F0) | > 1000 | hr | IEC 60811-406 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 1 sec) | 53 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Break | 28.0 | MPa | ISO 527-2 |
| Break, 23°C 1 | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Break | 800 | % | ISO 527-2 |
| Break, 23°C 2 | 500 | % | ISO 527-2/50 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -76.0 | °C | ISO 974 |
| Hot Set - 15 min, 0.2 MPa 3(200°C) | 60 | % | IEC 60811-507 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.30 | ASTM D1531 | |
| Dissipation Factor (1 MHz) | 7.0E-5 | ASTM D1531 |
| Note Message | |
|---|---|
| 1 . | Crosslinked Compound |
| 2 . | Crosslinked Compound |
| 3 . | Crosslinked Compound |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE ICP5008 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| Axiall PVC UV-6685 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| DESLON™ 66 DSC201G10 | DESCO Co., Ltd. | Nylon 66 | DESLON™ 66 |
| Later 4 | LATI S.p.A. | PBT | Later |
| Petrothene® NA860008 | LyondellBasell Industries | LDPE | Petrothene® |