TECHNYL® A 218HPS V35 BLACK 21N Datasheet,Nylon 66/6,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL® A 218HPS V35 is a polyamide blend of polyamide 6.6 polyamide 6 reinforced with 35% of glass fiber, high heat stabilized for injection moulding. This grade is designed to offer a long term heat resistance and is suitable to work in environments characterized by a very high temperature. (210°C)

General Information
Filler / Reinforcement	Glass fiber reinforced material, 35% filler by weight
Additive	heat stabilizer
Features	Heat Stabilized - Inorganic Excellent appearance High liquidity
Uses	Application in Automobile Field
Agency Ratings	EC 1907/2006 (REACH)
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1)
Resin ID (ISO 1043)	PA66+PA6-GF35

Physical	Nominal Value	Unit	Test Method
Density	1.42	g/cm³	ISO 1183/A

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	11600	MPa	ISO 527-2/1A
Tensile Stress (Break, 23°C)	196	MPa	ISO 527-2/1A
Tensile Strain (Break, 23°C)	3.4	%	ISO 527-2
Flexural Modulus (23°C)	9880	MPa	ISO 178
Flexural Stress (23°C)	306	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	13	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	88	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	247	°C	ISO 75-2/Bf
1.8 MPa, not annealed	224	°C	ISO 75-2/Af
Melting Temperature	248	°C	ISO 11357-3

Injection	Nominal Value	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	270 - 280	°C
Middle Temperature	275 - 285	°C
Front Temperature	280 - 290	°C
Mold Temperature	70 - 100	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL® RED
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	VQWByO_TECHNYLA218HPSV35BLACK21N.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
DAI-EL™ G-901	DAIKIN AMERICA, INC.	Fluorelastomer	DAI-EL™
Grilamid® XE 4073 nat	EMS-GRIVORY	Nylon 610	Grilamid®
Escorene™ Ultra LD 713.93 Cast	ExxonMobil Chemical	EVA	Escorene™ Ultra
Wuxi Jiahong EB-2133	Wuxi Jiahong Plastics Technology CO., Ltd.	PVC, Unspecified	Wuxi Jiahong
POCAN® B 3233 HR 000000	LANXESS GmbH	PBT	POCAN®