LNP™ LUBRICOMP™ YI001 compound
| Category: | TPEE , Thermoplastic Polyester Elastomer |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VMesaL_LNP-LUBRICOMP-YI001-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP YI001 is a compound based on Polyester Elastomer containing Silicone. Added features include; Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound YL-4410 NAT Product reorder name: YI001 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 2.1 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.60 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 185 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 14.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 37 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 185 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 9.00 | MPa | |
| -- 4 | 12.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5(23°C) | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 193 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 83.0 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.0E-4 | cm/cm/°C | |
| Transverse : 23 to 60°C | 2.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 182 to 193 | °C | |
| Middle Temperature | 204 to 216 | °C | |
| Front Temperature | 227 to 238 | °C | |
| Processing (Melt) Temp | 216 to 238 | °C | |
| Mold Temperature | 26.7 to 54.4 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Break |
| 4 . | Yield |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® GS5073 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Xuchuan XCW-6380B | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| AKROTEK® PEEK TM black (5051) | AKRO-PLASTIC GmbH | PEEK | AKROTEK® |
| Sylvin 8960-65FUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Braskem PE SLL118/21 | Braskem | LLDPE | Braskem PE |