Celanex® 3309HRHF
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celanex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | VB0iUr_Celanex-3309HRHF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celanex 3309HRHF is a 30% fiberglass reinforced Polybutylene Terephthalate which has excellent hydrolysis resistance, mechanical properties and improved flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.70 - 1.2 | % | ISO 294-4 |
| Flow direction | 0.10 - 0.30 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.16 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 9700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 220 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 9.1 | kJ/m² | ISO 179/1eA |
| 23°C | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 39 | kJ/m² | ISO 179/1eU |
| 23°C | 44 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 222 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 210 | °C | ISO 75-2/A |
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.9E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 2.80 | IEC 60250 | |
| 1 MHz | 3.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | IEC 60250 | |
| Comparative Tracking Index | 254 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 230 - 240 | °C | |
| Middle Temperature | 235 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 250 - 260 | °C | |
| Processing (Melt) Temp | 235 - 260 | °C | |
| Mold Temperature | 65.0 - 93.0 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.00 - 0.345 | MPa |
| Injection instructions |
|---|
| Screw Speed: Medium |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP561X | PolyMirae | PP, Unspecified | Moplen |
| NEFTEKHIM PP 8548S (EPH71HA) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Chemiton NA I2NA 50 | Franplast S.r.l. | SEBS | Chemiton |
| GPPC PS-316 | GPPC Chemical Co., Ltd. | PS (HIPS) | GPPC |
| LARIPUR® LPR 9025 | COIM S.p.A. | TPU-Polyester | LARIPUR® |