Resinoid 1345
| Category: | Phenolic , Phenolic |
| Manufacturer: | Resinoid Engineering Corporation |
| Trademark: | Resinoid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | V9lGT2_Resinoid-1345.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Resinoid 1345 is a glass reinforced, two-step phenolic molding compound. It was specifically developed for molded electric motor commutators where performance for prolonged periods at elevated temperatures while under centrifugal loads is critical. This material comes in pelletized from and is suitable for injection, transfer or compression molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.00 | g/cm³ | ASTM D792A, ISO 1183 |
| Bulk Factor | 2.5 | ASTM D1895 | |
| Molding Shrinkage | |||
| Flow | 0.10 | % | ASTM D955 |
| Flow direction | 0.10 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr | 0.10 | % | ASTM D570 |
| 23°C, 24 hr | 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| E scale | 90 | ASTM D785 | |
| Class m | 110 | ASTM D785 | |
| M scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 58.6 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2 |
| Flexural Modulus | |||
| -- | 15200 | MPa | ASTM D790 |
| -- | 15000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 82.7 | MPa | ASTM D790 |
| -- | 83.0 | MPa | ISO 178 |
| Compressive Strength | 186 | MPa | ASTM D695, ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 69 | J/m | ASTM D256A |
| -- | 6.8 | kJ/m² | ISO 180/2A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 300 | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 2.7E-5 | cm/cm/°C | ASTM D696, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 12 | kV/mm | ASTM D149, IEC 60243-1 |
| Arc Resistance | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Additional Information |
|---|
| Bulk Factor, ISO 171: 2 to 3Bulk Factor, ASTM D955: 2 to 3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 132 HF | RTP Company | PP, Unspecified | RTP |
| Bayflex® 110-35 IMR (18% Mineral) | Covestro - PUR | PUR-Ether/MDI | Bayflex® |
| LNP™ STAT-KON™ RX04031 compound | SABIC Innovative Plastics Europe | Nylon 66 | LNP™ STAT-KON™ |
| POLYCOMPO PE 6200B | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |
| Lifoflex® UV FLAM 40700 | Müller Kunststoffe GmbH | TPE | Lifoflex® |