Riblene® FF 33
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6AYwGi_RibleneFF33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FF 33 is a high molecular weight low density polyethylene (LDPE), additivated with slip agent, ideal for blown film extrusion. Riblene FF 33 is characterised by a good melt strength leading to a good bubble stability during extrusion. Main Applications Riblene FF 33 is recommended for the production of shrink film for medium and light loads, for lamination film, for carrier bags, for packaging film and for blend. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Dynamic, Blown Film) | 0.11 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 70 | µm | |
| Film Thickness - Recommended / Available | 30 to 120 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% sectioning, MD : 70 µm, blown film | 180 | MPa | ISO 527-3 |
| 1% sectioning, TD : 70 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : yield, 70 µm, blow film | 10.0 | MPa | ISO 527-3 |
| TD : yield, 70 µm, blow film | 11.0 | MPa | ISO 527-3 |
| MD : broken, 70 µm, blown film | 22.0 | MPa | ISO 527-3 |
| TD : broken, 70 µm, blown film | 19.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : broken, 70 µm, blown film | 400 | % | ISO 527-3 |
| TD : broken, 70 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact 1(70 µm, Blown Film) | 180 | g | ISO 7765-1/A |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 45.0 | kN/m | ISO 6383-2 |
| TD : 70.0 µm | 60.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 113 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 70.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 7.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 200 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4092 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Premi-Glas® 1200H-30 | Premix, Inc. | TS, Unspecified | Premi-Glas® |
| KumhoSunny ABS 790S | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| POLYFLAM® SDR 5005 WHITE 88315 HP25 | A. Schulman Europe | PS (GPPS) | POLYFLAM® |
| NORYL GTX™ GTX678 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |