TOPAS® 9506F-04
| Category: | COC , Cyclic Olefin Copolymer |
| Manufacturer: | Polyplastics Co., Ltd. |
| Trademark: | TOPAS® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UppFNu_TOPAS-9506F-04.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Film grade |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.00 | cm³/10min | |
| 230°C/2.16 kg | 6.00 | cm³/10min | |
| Water Absorption (Saturation, 23°C) | 0.010 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1A/1 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-3 | ||
| MD | 1700 | MPa | |
| TD | 2000 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break | 55.0 | MPa | |
| TD : Break | 55.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break | 2.9 | % | |
| TD : Break | 3.6 | % | |
| Dart Drop Impact 1 | < 36 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD | 2.3 | N | |
| TD | 2.4 | N | |
| Oxygen Permeability (23°C, 50% RH) | 17 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 90% RH) | 0.080 | g·mm/m²/atm/24 hr | ISO 15106-3 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 2 | 65.0 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | > 100 | ISO 2813 | |
| Haze | < 1.0 | % | ISO 14782 |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® 9417 | Covestro - Polycarbonates | PC | Makrolon® |
| Maxxam™ PPH-10G Nat | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Spartech Polycom SP7210 | Spartech Polycom | PC | Spartech |
| Chemical Resources PP 3700 | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| Dryflex® T40 | ELASTO | TPE | Dryflex® |