| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | USI Corporation |
| Trademark: | UNITHENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UighLE_UNITHENE-LH514.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UNITHENE LH514 (HDPE)having high melt flow index suitable used for injection molding and the applications are thin and smart housewares, toys, etc. UNITHENE LH514 possesses good processability, high impact strength and good resistance to stress cracking, good stiffness, high hardness, good surface gloss, less warpage, low shrinkage. UNITHENE LH514 can be easily pigmented to any color by either dry blending or melt blending of the pigment into the resin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.956 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 12 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - 1% Secant (Compression Molded) | 765 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 24.5 | MPa | ASTM D638 |
| Fracture | 17.7 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 550 | % | ASTM D638 |
| Apparent Bending Modulus | 814 | MPa | ASTM D747 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Peak Melting Temperature | 132 | °C | ASTM D3418 |
| Additional Information |
|---|
| Torsional Stiffness, ASTM D1043: 9600 kg/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENELENE® 2213 | Poliolefinas Internacionales, C.A. (Polinter) | LLDPE | VENELENE® |
| ABSCOM® S106 | Polymer Compounders Limited | ABS | ABSCOM® |
| Nypol® PA A3 G50 HS RH PRTA012 NR439 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Braskem PP CP 295 | Braskem | PP Impact Copolymer | Braskem PP |
| Kazan LDPE 16813-070 OKP 22 111 4101 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |