LNP™ THERMOCOMP™ MB008S compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | UhA6q0_LNP-THERMOCOMP-MB008S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MB008S is a compound based on Polypropylene resin containing 40% Glass Bead. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MB-1008 HS Product reorder name: MB008S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | |||
| -- | 1.21 | g/cm³ | ISO 1183 |
| -- | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 1.2 to 1.4 | % | ASTM D955 |
| Across Flow : 24 hr | 1.3 to 1.5 | % | ASTM D955 |
| Across Flow : 24 hr | 1.4 | % | ISO 294-4 |
| Flow : 24 hr | 1.3 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 1660 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 19.3 | MPa | ASTM D638 |
| Yield | 19.0 | MPa | ISO 527-2 |
| Break | 15.9 | MPa | ASTM D638 |
| Break | 15.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 6.0 | % | ASTM D638 |
| Yield | 6.2 | % | ISO 527-2 |
| Break | 160 | % | ASTM D638 |
| Break | 44 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2070 | MPa | ASTM D790 |
| -- | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 27.6 | MPa | ASTM D790 |
| -- | 36.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 27 | J/m | ASTM D256 |
| 23°C 2 | 2.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D4812 |
| 23°C 3 | 16 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 6.00 | J | ASTM D3763 |
| -- | 1.80 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 103 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 60.6 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 61.0 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 7.2E-6 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.7E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 7.2E-6 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Silicone SI 9045C | Sumitomo Bakelite North America, Inc. | Silicone | Sumitomo Silicone |
| NEFTEKHIM PP 7648H | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Jamplast JPPCABSI | Jamplast, Inc. | PC+ABS | Jamplast |
| Elastoprene HS5060A NAT | KMI Group, Inc. | TPE | Elastoprene |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 6213 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |