China PPS hMR60
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Sichuan Deyang Chemical Co., Ltd |
| Trademark: | China PPS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | U7WFBd_China-PPS-hMR60.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PPS-hMR60 is filled and reinforced PPS compound, which is filled with mineral and glass fiber based on the PPS resin. With a comparative low price, it shows high rigidity, creep resistance, low mold shrinkage, high-temperature resistance, inherent flame resistance, excellent electrical insulation properties, easy processing, and good dimensional stability. Owing to its high performance and comparative low price, it is widely used in electronic, electric appliances, automobile, home appliances, railway, space aviation, mechanical and military fields etc. Such as: connectors, plugs, lamp holders, electric appliance outer shells where high-temperature resistant is required, nuts, bolts and contacting panel of electric appliance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.92 | g/cm³ | Internal method |
| Molding Shrinkage | Internal method | ||
| Flow | 0.25 | % | Internal method |
| Transverse flow | 0.75 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness 1 | 110 | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 172 | MPa | Internal method |
| Tensile Elongation (Break) | 1.3 | % | Internal method |
| Flexural Modulus | 15400 | MPa | Internal method |
| Flexural Strength | 257 | MPa | Internal method |
| Compressive Strength | 140 | MPa | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 10 | kJ/m² | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 265 | °C | Internal method |
| Melting Temperature | 282 | °C | Internal method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+14 | ohms | Internal method |
| Volume Resistivity | 2.0E+16 | ohms·cm | Internal method |
| Dielectric Strength | 15 | kV/mm | Internal method |
| Dielectric Constant (1 MHz) | 4.00 | Internal method |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 140 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 300 - 320 | °C | |
| Front Temperature | 300 - 320 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Processing (Melt) Temp | 160 - 180 | °C | |
| Mold Temperature | 100 - 150 | °C | |
| Injection Pressure | 50.0 - 100 | MPa | |
| Back Pressure | 0.100 - 1.00 | MPa | |
| Screw Speed | 40 - 100 | rpm |
| Injection instructions |
|---|
| Processing time: 4 to 16hr |
| Note Message | |
|---|---|
| 1 . | HR |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G13P100-00 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Soarnol® BX6304B | Soarus L.L.C. | EVOH | Soarnol® |
| NEFTEKHIM PP 8300E | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| BJB Epoxy TC-1651 A/B | BJB Enterprises, Inc. | Epoxy | BJB Epoxy |
| Braskem PE SHC7260LS-L | Braskem America Inc. | HDPE | Braskem PE |