POLYblend PC/ABS 65CI
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polykemi AB |
| Trademark: | POLYblend |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | TYBZ2a_POLYblend-PC-ABS-65CI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC/ABS-blend |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.50 to 0.70 | % | |
| Flow | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 48.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 6.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2100 | MPa | ISO 178 |
| Flexural Stress | 77.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 56 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 1 | |||
| 0.45 MPa, Unannealed | 109 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 111 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 91.0 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 100 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 123 | °C | ISO 306/A50 |
| -- | 105 | °C | ISO 306/B50 |
| Ball Pressure Test (95°C) | Pass | IEC 60695-10-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-37168 | Teknor Apex Company | TPE | Monprene® |
| HAIPLEN H50 T8 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| LNP™ LUBRICOMP™ LL004C compound | SABIC Innovative Plastics | PEEK | LNP™ LUBRICOMP™ |
| Lupoy® GN5001RFG | LG Chem Ltd. | PC+ABS | Lupoy® |
| PEEK-OPTIMA® Unfilled | Invibio Inc. | PEEK | PEEK-OPTIMA® |