INEOS PP H03G-05
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ScCGdi_INEOS-PP-H03G-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| H03G-05 is a polypropylene homopolymer designed for BOPP applications and meets the requirements of the U.S. Food and Drug administration as specified in 21 CFR 177.1520. This high strength, barefoot resin has good optical properties and consistent, high speed processing. Typical applications are: Food Packaging, Overwrap and Metallized Film. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.4 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 32.8 | MPa | |
| Break | 19.2 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 13 | % | |
| Break | 140 | % | |
| Flexural Modulus - 1% Secant | 1350 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 42 | J/m | ASTM D256 |
| Notched Izod Impact (Area) (23°C) | 4.11 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 88.3 | °C | ASTM D648 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°) | 95 | ASTM D2457 | |
| Haze 3(1270 µm) | 72 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fibrolon® P 7550 | FKuR Kunststoff GmbH | Polyolefin, Unspecified | Fibrolon® |
| Karina IVORY PVC COMPOUND -E 90900-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ RF008H compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Osterlene® HB0554 | Osterman & Company | HDPE | Osterlene® |
| POCAN® KU 2-7317 000000 | LANXESS GmbH | PBT | POCAN® |