Hyundai EP Adhesives LE102T/1002
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | HYUNDAI EP Co., Ltd. |
| Trademark: | Hyundai EP Adhesives |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SVXBnH_Hyundai-EP-Adhesives-LE102T-1002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hyundai EP Adhesives LE102T/1002 is a Polyethylene product. It is available in Asia Pacific. Applications of Hyundai EP Adhesives LE102T/1002 include adhesives/tapes and coating applications. |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.935 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Water Absorption (24 hr) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 38 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 17.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 800 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 90.0 | °C | ASTM D1525 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion Strength | > 4.9 | kN/m | Internal Method |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® 1002C | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| Sinpolene GPP1640 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| Terraloy™ MB-20001A | Teknor Apex Company | TPS+Copolyester | Terraloy™ |
| ExxonMobil™ LDPE LD 200.48 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Karina WHITE PVC COMPOUND 105905-10/ 96-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |