Amodel® A-8422 LS WH159
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Amodel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | raghYg_Amodel-A-8422-LS-WH159.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Amodel® A-8422 LS is a light-stabilized, high-reflectivity, 22%-reinforced white polyphthalamide (PPA) that exhibits high heat resistance, high strength and stiffness over a broad temperature range, low moisture absorption, excellent chemical resistance, and excellent electrical properties.
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183/A |
| Mold Shrinkage | |||
| Vertical flow direction | 1.0 | % | |
| Flow direction | 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile fracture strain | 0.95 | % | ASTM D638 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Light reflectivity | ASTM E1331 | ||
| 460 nm | > 90 | % | ASTM E1331 |
| 540 nm | > 90 | % | ASTM E1331 |
| 615 nm | > 90 | % | ASTM E1331 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 11000 | MPa | ASTM D638 |
| -- | 10900 | MPa | ISO 527-2 |
| Tensile Strength | |||
| -- | 95.1 | MPa | ASTM D638 |
| -- | 102 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10200 | MPa | ASTM D790 |
| -- | 9930 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 168 | MPa | ASTM D790 |
| -- | 145 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 2.7 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Annealed) | 280 | °C | ISO 75-2/B |
| Melting Temperature | 327 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow : 50 to 100°C | 2.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 100 to 150°C | 2.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : 150 to 200°C | 2.1E-5 | cm/cm/°C | ASTM E831 |
| Flow : 200 to 250°C | 2.7E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 50 to 100°C | 5.1E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 100 to 150°C | 7.3E-5 | cm/cm/°C | ASTM E831 |
| Horizontal : 150 to 200°C | 1.1E-4 | cm/cm/°C | ASTM E831 |
| Horizontal : 200 to 250°C | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.045 | % | |
| Rear Temperature | 304 - 318 | °C | |
| Front Temperature | 316 - 329 | °C | |
| Processing (Melt) Temp | 321 - 343 | °C | |
| Mold Temperature | 135 | °C |
| Injection instructions |
|---|
| A general purpose screw is recommended, with minimum back pressure.Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC7PCZ (Series: AD/PA/CS) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Borealis PP RB206MO | Borealis AG | PP Random Copolymer | Borealis PP |
| Braskem PE ML2400N | Braskem | LLDPE | Braskem PE |
| Fainplast PVC MPH 83 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hostacom G3 U01 102297 | LyondellBasell Industries | PP Copolymer | Hostacom |