BJB Polyurethane TC-262 A/B
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SRRoYS_BJB-Polyurethane-TC-262-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-262 A/B is a two-component water blown flexible semi-viscoelastic polyurethane foam system specifically developed for low-density molding. Nominal density of the finished product is in the range of 5-6 pounds per cubic foot, when open blown or not restricted. Higher densities may be obtained in closed or restricted mold. BJB's 6800 Series Pigments may be added to the "B"side for developing a wide range of colors. TC-262 A/B can be hand mixed, machine dispensed, or mixed with a Jiffy Mixer®. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| Part A : 25°C | 1.187 | g/cm³ | |
| Part B : 25°C | 1.017 | g/cm³ | |
| Density | 80.1 to 96.1 | kg/m³ |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Cream Time (25°C) | 20.0 to 30.0 | sec | |
| Rise Time | 2.5 to 3.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity | |||
| Part A : 25°C | 205 | mPa·s | |
| Part B : 25°C | 620 | mPa·s |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Cure Time (25°C) 1 | 20.0 to 30.0 | min |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 33 | ||
| Part B | Mix Ratio by Weight: 100 | ||
| Shelf Life | 26 | wk |
| Note Message | |
|---|---|
| 1 . | Depending on part size and cross section |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL AH-GP1 | Polymer Resources Ltd. | Acetal (POM) Homopolymer | PRL |
| Kepital® F20-51 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Hostacom EKC 265N G51359 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Latamid 66 VH2 G/30 | LATI S.p.A. | Nylon 66 | Latamid |
| Karina CLEAR PVC COMP. -E 87/206-D-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |