LNP™ VERTON™ RV008S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SQ29pG_LNPVERTONRV008Scompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RV008S is a compound based on Nylon 66 resin containing Long Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* VERTON* Compound RF-7008 HS Product reorder name: RV008S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 13900 | MPa | ASTM D638 |
| Tensile Strength (Break) | 241 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 360 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 970 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 262 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROLON 3011 | Taro Plast S.p.A. | PC | TAROLON |
| Cariflex® IR0401 SU | Kraton Polymers LLC | IR | Cariflex® |
| Daelim Po1y® HX-250BL | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| DOMAMID® 6S | DOMO Engineering Plastics SPA | Nylon 6 | DOMAMID® |
| Generic PC+Polyester - Glass Fiber | Generic | PC+Polyester | Generic |