PBT, 30 % glass fibers, injection molding, improved impact strength

General Information
Filler / Reinforcement	Glass Fiber, 30% Filler by Weight
Features	Good Impact Resistance
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.46	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/5.0 kg)	13.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 2577
Across Flow : 260°C, 2.00 mm ¹	0.90	%
Across Flow : 120°C, 4 hr, 2.00 mm ²	0.20	%
Flow : 260°C, 2.00 mm ³	0.40	%
Flow : 120°C, 4 hr, 2.00 mm ⁴	0.10	%
Water Absorption			ISO 62
Saturation, 23°C	0.40	%
Equilibrium, 23°C, 50% RH	0.20	%

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	160	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	8000	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	95.0	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	4.0	%	ISO 527-2/5
Flexural Modulus ⁵(23°C)	7600	MPa	ISO 178/A
Flexural Stress			ISO 178/A
3.5% Strain, 23°C	155	MPa
23°C ⁶	160	MPa
Flexural Strain at Flexural Strength ⁷(23°C)	3.8	%	ISO 178/A

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion (23°C)	A 1		IEC 60426
ISO Shortname	PBT, GHMPR, 09-080, GF30		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 to 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	10	kJ/m²
23°C	12	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	65	kJ/m²
23°C	65	kJ/m²
Notched Izod Impact Strength			ISO 180/1A
-40°C	< 10	kJ/m²
-30°C	10	kJ/m²
23°C	12	kJ/m²
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	55	kJ/m²
23°C	55	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	220	°C	ISO 75-2/B
1.8 MPa, Unannealed	195	°C	ISO 75-2/A
Vicat Softening Temperature	185	°C	ISO 306/B120
Ball Pressure Test (210°C)	Pass		IEC 60695-10-2
Melting Temperature ⁸	225	°C	ISO 11357-3
CLTE			ISO 11359-2
Flow : 23 to 55°C	3.0E-5	cm/cm/°C
Transverse : 23 to 55°C	1.0E-4	cm/cm/°C
Thermal Conductivity (23°C)	0.27	W/m/K	ISO 8302

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity (23°C)	> 1.0E+14	ohms·cm	IEC 60093
Electric Strength (23°C, 1.00 mm)	28	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	4.60
23°C, 1 MHz	3.90
Dissipation Factor (23°C, 1 MHz)	0.026		IEC 60250
Comparative Tracking Index (Solution A)	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.800 mm	HB
1.60 mm	HB
Glow Wire Flammability Index (2.00 mm)	650	°C	IEC 60695-2-12
Oxygen Index ⁹	21	%	ISO 4589-2

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 to 8.0	hr
Processing (Melt) Temp	250 to 270	°C
Mold Temperature	80.0 to 100	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min
9 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X4265	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
MARPOL® EVA 2806	Marco Polo International, Inc.	EVA	MARPOL® EVA
VERSIFY™ 4301	The Dow Chemical Company	TPO (POE)	VERSIFY™
Cellidor B 500-15	ALBIS PLASTIC GmbH	CAB	Cellidor
DSR TL-8080	Dragon Special Resin (Xiamen) Co., Ltd.	PET	DSR