Kepamid® 2315GVS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | SFhowG_Kepamid-2315GVS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KEPAMID 2315GVS is a 15% glass fiber reinforced and flame retardant polamide-66. Flame resistance recognized as UL94 V-0 rating with good mechanical and thermal properties. It is applicable to automotive, electrical, electronic, and industrial parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 to 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 108 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 6960 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 260 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 260 to 290 | °C | |
| Rear Temperature | 260 to 290 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 260 to 290 | °C | |
| Nozzle Temperature | 260 to 290 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2770 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| VESTAMID® HTplus M3000 NC | Evonik Industries AG | PPA | VESTAMID® HTplus |
| ARC ARC10H | ARC Resin Corporation | Acetal (POM) Homopolymer | ARC |
| Huafon HF-1195A | Huafon Group Co., Ltd. | TPU-Polyester | Huafon |
| Sylvin 9940-90 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |