SABIC® LDPE 2100TN21
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | RVY1dx_SABIC-LDPE-2100TN21.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2100TN21 is a grade with excellent toughness and tear strength and outstanding shrink properties. The material contains anti block and slip erucamide, has a very low energy consumption during processing and has good draw down properties. SABIC® LDPE 2100TN21 is suitable for application in shrinkhoods, industrial sacks, heavy duty carrier bags and liners. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.33 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.20 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 190 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : 50 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength (50.0 µm) 1 | 300 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking (50.0 µm) 2 | 10 | g | Internal method |
| Re-blocking (50.0 µm) 3 | 10 | g | Internal method |
| Tear Strength 4 | ISO 6383-2 | ||
| MD : 50.0 µm | 45.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 25.0 | kN/m | ISO 6383-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 15 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Films have been produced on Kiefel IBC film blown line at 200 kg/h with a die of 200 mm and a die gap of 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Film |
| 3 . | Blown Film |
| 4 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAZMID B 150 FV20 EV10 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 6 | MAZMID B |
| Sup-tech H703 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 46 | Sup-tech |
| ADEKA QR-9466 | Adeka Corporation | Epoxy | ADEKA |
| Estane® 2103-80AE TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| LubriOne™ PC-000/15T-S2 NATURAL | PolyOne Corporation | PC | LubriOne™ |