MAGNUM™ 1250 BG
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 4aGS3K_MAGNUM-1250-BG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High Impact, High Heat, Blow Molding ABS |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 1.7 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 1.7 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 33.6 | MPa | ASTM D638 |
| Yield | 33.7 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 60 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 2010 | MPa | ASTM D790 |
| -- | 1810 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -29°C | 190 | J/m | ASTM D256 |
| 23°C | 360 | J/m | ASTM D256 |
| -30°C | 17 | kJ/m² | ISO 180 |
| 23°C | 26 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 103 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 101 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 86.7 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 85.0 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Stirofor® HI-V2 NATURALE | SO.F.TER. SPA | PS (HIPS) | Stirofor® |
| ETILINAS BPD 4028 | POLYETHYLENE MALAYSIA SDN BHD | MDPE | ETILINAS |
| Elastollan® R 2000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Emulprene® 1011 | INSA | SBR, Emulsion | Emulprene® |
| Hyundai EP PA66 LD460 | HYUNDAI EP Co., Ltd. | Nylon 66 | Hyundai EP PA66 |