Lupol® GP3300
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QukEDg_Lupol-GP3300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LUPOL GP-3303 is designed for injection molding of large parts by reinforced with mineral filler. This product features excellent dimensional stability and low warpage characteristics, thus ideal for interior materials of automobiles, and electric/electronic parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 - 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 35.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 20 | % | ASTM D638 |
| Flexural Modulus | 3430 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 54.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 29 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 145 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 95.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Hopper Temperature | 50.0 - 57.0 | °C | |
| Rear Temperature | 190 - 210 | °C | |
| Middle Temperature | 207 - 222 | °C | |
| Front Temperature | 211 - 228 | °C | |
| Nozzle Temperature | 205 - 220 | °C | |
| Mold Temperature | 50.0 - 57.0 | °C | |
| Injection Pressure | 2.94 - 11.8 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 1.47 - 5.88 | MPa | |
| Screw Speed | 40 - 60 | rpm |
| Injection instructions |
|---|
| Secondary Injection Pressure: 20 to 100 kg/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 4824WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| Chemical Resources PP 3000 | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| OXNILON 6 50GF | Oxford Polymers | Nylon 6 | OXNILON 6 |
| PENTAMID A GV50 H Rot 3020/1 | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |
| LEXAN™ LUX2289 resin | SABIC Innovative Plastics | PC | LEXAN™ |