POLYFLAM® RMMB 40400
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QlqqqC_POLYFLAM-RMMB-40400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant ABS/PC blend for higher temperature resistance and impact strength; halogen free according to DIN VDE 0472 part 815 |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 28.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 21 | kJ/m² | ISO 179/1eA |
| 23°C | 63 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 95.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 115 | °C | ISO 306/A50 |
| -- | 110 | °C | ISO 306/B50 |
| Ball Pressure Test (105°C) | Pass | IEC 60695-10-2 | |
| RTI Elec | UL 746 | ||
| 1.50 mm | 60.0 | °C | UL 746 |
| 3.00 mm | 60.0 | °C | UL 746 |
| RTI Imp | UL 746 | ||
| 1.50 mm | 60.0 | °C | UL 746 |
| 3.00 mm | 60.0 | °C | UL 746 |
| RTI | UL 746 | ||
| 1.50 mm | 60.0 | °C | UL 746 |
| 3.00 mm | 60.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 600 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 3 | UL 746 | |
| 3.00 mm | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | UL 746 | |
| 3.00 mm | PLC 2 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | ISO 3795 | ||
| 1.50mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| 3.50, automatic fire extinguishing | 0.0 | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 1.50 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 | UL 94, IEC 60695-11-10, -20 | |
| 3.50 mm | V-0 5VA | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.50 mm | 960 | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | °C | IEC 60695-2-12 |
| 3.50 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.50 mm | 800 | °C | IEC 60695-2-13 |
| 3.00 mm | 800 | °C | IEC 60695-2-13 |
| 3.50 mm | 800 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 250 | °C | |
| Middle Temperature | 270 | °C | |
| Front Temperature | 270 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HM-283 | Ravago Manufacturing Americas, LLC | PE, Unspecified | Ravago Compounds |
| SUSTADUR PET | Röchling Sustaplast SE & Co. KG | PET | SUSTADUR |
| DJSilicone NE-351 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| PENTAMID AB L5 H1 RC schwarz | PENTAC Polymer GmbH | Nylon 66/6 | PENTAMID AB |
| POCAN® B 1300 000000 | LANXESS Corporation | PBT | POCAN® |