LNP™ LUBRICOMP™ RA004 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QioM91_LNPLUBRICOMPRA004compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RA004 is a compound based on Nylon 66 resin containing Aramid Fiber. Also known as: LNP* LUBRICOMP* Compound RA1004 Product reorder name: RA004 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 85.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4000 | MPa | ISO 178 |
| Flexural Stress | 122 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 199 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (0.800 mm) | 550 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 277 - 288 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8478-70FUV Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Vipel® F701-PTT-25 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Multi-Flex® TPE A7455 S | Multibase, A Dow Corning Company | TPE | Multi-Flex® TPE |
| Gebablend 65 HI | geba Kunststoffcompounds GmbH | PC+ABS | Gebablend |
| ULTEM™ 3452 resin | SABIC Innovative Plastics | PEI | ULTEM™ |