UPES® 315-LR
| Category: | PS+PE , Polystyrene + PE |
| Manufacturer: | NOVA Chemicals |
| Trademark: | UPES® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | DYVz32_UPES-315-LR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UPES® 315-LR is a Polystyrene + PE (PS+PE) material. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D6226 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.35 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(Injection Molded) | 2220 | MPa | ASTM D638 |
| Tensile Strength 2(Break, Injection Molded) | 36.8 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, Injection Molded) | 3.3 | % | ASTM D638 |
| Flexural Modulus (Injection Molded) | 1800 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, Injection Molded) | 53.8 | MPa | ASTM D790 |
| Flexural Strain - Yield 5 | > 5.1 | % | ASTM D790 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Shrink Ratio | < 1.00 | ASTM D955 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Injection Molded) | 23 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 101 | °C | ASTM D1525 6 |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | 5.1 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 0.05 in/min, Injection Molded |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren I180E (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| APEX® 7500-90 | Teknor Apex Company | PVC, Flexible | APEX® |
| Lifoflex® UV 30 GB 1030 | ELASTO | SEBS | Lifoflex® |
| LNP™ LUBRICOMP™ QFL32 compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |
| Lupox® SG5150 | LG Chem Ltd. | PBT+PET | Lupox® |