CoolPoly® D8102
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Celanese Corporation |
| Trademark: | CoolPoly® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pgrhd9_CoolPoly-D8102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CoolPoly D series of thermally conductive plastics transfers heat, a characteristic previously unavailable in injection molding grade polymers. CoolPoly is lightweight, netshape moldable and allows design freedom in applications previously restricted to metals. The D series is electrically non-conductive and can be used for its dielectric properties. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.50 | % | ASTM D955 |
| Transverse flow | 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 45 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 2.25 | MPa | ISO 37 |
| Tensile Elongation (Break) | 73 | % | ISO 37 |
| Tear Strength 1 | 12 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat | 1750 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 3.0 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 2.64 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.36 mm) | HB | UL 94 |
| Additional Information |
|---|
| The value listed as Thermal Conductivity, ASTM C177, was tested in accordance with ASTM E1461.The value listed as Mold Shrinkage, ASTM D955, was tested in accordance with ASTM D551.The value listed as Specific Heat ASTM C351, was tested in accordance with ASTM E1461.Thermal Diffusivity, ASTM E1461: 0.0144 cm²/sec |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 | °C | |
| Drying Time | 2.0 | hr | |
| Dew Point | -18.0 | °C | |
| Rear Temperature | 180 - 205 | °C | |
| Middle Temperature | 195 - 230 | °C | |
| Front Temperature | 200 - 240 | °C | |
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 40.0 - 65.0 | °C | |
| Injection Pressure | 21.0 - 50.0 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 3.50 - 35.0 | MPa | |
| Back Pressure | 0.00 - 0.350 | MPa | |
| Screw Speed | 40 - 65 | rpm | |
| Screw Compression Ratio | 2.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mediprene® 502484M | ELASTO | TPE | Mediprene® |
| SITRAMAC 5E-IM-UV / C14/6 satine | SITRAPLAS GmbH | Acrylic (PMMA) | SITRAMAC |
| Colorite 12 Series 9812 | Colorite Polymers | PVC, Unspecified | Colorite 12 Series |
| Kingfa PBT RG302 | Kingfa | PBT | Kingfa PBT |
| LUVOCOM® 16-0665 | Lehmann & Voss & Co. | PARA | LUVOCOM® |