Amodel AS- 4133 L 33% glass fiber reinforced, lubricated, structural grade polyphthalamide (PPA), fast processing cycle, warm water can be formed. Conventional uses include electrical and electronic components. -Black: AS-4133 L BK 324 natural color: AS-4133 L NT

General Information
Filler / Reinforcement	Glass fiber reinforced material, 33% filler by weight
Additive	Lubricant
Features	Good dimensional stability Low hygroscopicity Rigid, good High strength Fast molding cycle Good creep resistance Good chemical resistance Hot water formability Lubrication
Uses	Electrical/Electronic Applications Power/other tools Valve/valve components Industrial application Thick wall fittings (parts) Machine/mechanical parts Metal substitution Parts under the hood of a car Automotive Electronics Application in Automobile Field Mobile phone General Shell
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Water temperature mold injection molding

Physical	Dry	Conditioned	Unit	Test Method
Specific Gravity	1.45	--	g/cm³	ASTM D792, ISO 1183/A
Molding Shrinkage				ASTM D955
Flow	0.50	--	%	ASTM D955
Transverse flow	1.0	--	%	ASTM D955
Water Absorption ¹(23°C, 24 hr)	0.29	--	%	ASTM D792

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus	11700	11700	MPa	ASTM D638
Tensile Strength (Break)	200	172	MPa	ASTM D638
Tensile Elongation (Break)	2.5	2.2	%	ASTM D638
Flexural Modulus	11000	11000	MPa	ASTM D790
Flexural Strength (Yield)	290	241	MPa	ASTM D790
Compressive Strength	179	172	MPa	ASTM D695
Shear Strength	90.0	75.8	MPa	ASTM D732
Poisson's Ratio	0.41	--		ASTM E132

Impact	Dry	Conditioned	Unit	Test Method
Notched Izod Impact	80	69	J/m	ASTM D256
Unnotched Izod Impact	960	--	J/m	ASTM D256

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load				ASTM D648
0.45 MPa, annealed, 3.18mm	320	--	°C	ASTM D648
1.8 MPa, annealed, 3.18mm	300	--	°C	ASTM D648
Melting Temperature	327	--	°C	ASTM D570, DSC
Linear thermal expansion coefficient				ASTM E831
Flow : 0 to 90°C	2.2E-5	--	cm/cm/°C	ASTM E831
Flow : 149 to 249°C	1.4E-5	--	cm/cm/°C	ASTM E831
Lateral : 0 to 90°C	5.9E-5	--	cm/cm/°C	ASTM E831
Lateral : 149 to 249°C	1.2E-4	--	cm/cm/°C	ASTM E831

Electrical	Dry	Conditioned	Unit	Test Method
Comparative Tracking Index (CTI)	600	600	V	UL 746
High Voltage Arc Tracking Rate (HVTR)	14.0	18.0	mm/min	UL 746

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating ²(3.18 mm)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	120 - 135	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.045	%
Rear Temperature	318 - 324	°C
Front Temperature	327 - 332	°C
Processing (Melt) Temp	329 - 343	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Note Message
1 .	General 0.29%, up to 1.07%
2 .	These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations.

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PXnpV5_Amodel-AS-4133-L.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
SEPAZ™ LB50	Mando Advanced Materials Co., Ltd.	Nylon 6	SEPAZ™
Sylvin 5199-80 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Ultraform® H 2320 006	BASF Corporation	Acetal (POM) Copolymer	Ultraform®
BLUESTAR® PBT 101G0	Nantong Zhonglan Engineering Plastics Co., Ltd.	PBT	BLUESTAR®
Chemlon® MDF4L	Teknor Apex Company (Chem Polymer)	Nylon 6	Chemlon®