Osterlene® HD0752

Category:	HDPE , High Density Polyethylene
Manufacturer:	Osterman & Company
Trademark:	Osterlene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PU8735_OsterleneHD0752.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

HD0752 is a high density polyethylene resin and is intended for use in injection molding applications such as pails, industrial parts and other shipping containers. This resin has been designed to provide excellent processability for molders and to meet the rigorous performance characteristics of applications requiring stackability, environmental stress crack resistance and impact strength.

Applications for HD0752 include injection molding, for injection molded pails, industrial parts and other shipping containers. This product has excellent impact strength, stress crack resistance and processability. It has a very narrow molecular weight distribution.

HD0752 has no slip, antiblock or processing aids.

HD0752 complies with U.S. FDA 21 CFR 177.1520 (c)3.1a, Canadian HPFB No Objection, EU, No 10/2011, U.S. USP, U.S. FDA DMF.

General Information
Features	High ESCR (Stress Cracking Resistance) Impact resistance, high Workability, good Narrow molecular weight distribution
Uses	Industrial application Container Barrel
Agency Ratings	FDA 21 CFR 177.1520(c) 3.1a
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.950	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	6.8	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50)	12.0	hr	ASTM D1693A

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	59		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
Yield	26.9	MPa	ASTM D638
Fracture	22.8	MPa	ASTM D638
Tensile Elongation			ASTM D638
Yield	7.0	%	ASTM D638
Fracture	1100	%	ASTM D638
Flexural Modulus - 2% Secant	1070	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Tensile Impact Strength	84.1	kJ/m²	ASTM D1822

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (0.45 MPa, Unannealed)	72.8	°C	ASTM D648
Brittleness Temperature	< -76.0	°C	ASTM D746
Vicat Softening Temperature	128	°C	ASTM D1525
Melting Temperature	131	°C	DSC
Peak Crystallization Temperature (DSC)	118	°C	Internal method

Resin Grade	Manufacturer	Category	Trademark
Thermylene® P6-30FM-0378	Asahi Kasei Plastics North America Inc.	PP, Unspecified	Thermylene®
North American Santicizer® 148	Ferro Corporation	Plasticizer	North
Lucent PP GPP-210	Lucent Polymers, Inc.	PP, Unspecified	Lucent PP
ALCUDIA® LDPE 2202-CN	REPSOL	LDPE	ALCUDIA® LDPE
3M™ Dyneon™ Fluoroelastomer FC 1640	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer