TAROMID A 260 Y0
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PLShVM_TAROMID-A-260-Y0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66/6 medium viscosity, flame retarded V0 halogen and phosphorus free. Low density, good flow and high tracking resistance. UL94 V0 listed all colors at 0,55 mm Available: different colors. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 to 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.0 to 1.5 | % | |
| Across Flow | 1.5 to 2.5 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 1.0 to 1.5 | % | ASTM D570, ISO 62 |
| Saturation | 8.0 | % | ASTM D570 |
| Saturation, 23°C | 8.0 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3600 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 95.0 | MPa | |
| Break | 85.0 | MPa | |
| Tensile Elongation (Break) | 6.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3300 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 135 | MPa | ISO 178 |
| Break | 135 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 2.5 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 2(23°C) | 50 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| -20°C, 3.20 mm | 25 | J/m | ISO 180 |
| 23°C, 3.20 mm | 40 | J/m | ISO 121 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 225 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 90.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 3 | 80.0 | °C | |
| -- 4 | 120 | °C | |
| Vicat Softening Temperature | |||
| -- | 248 | °C | ASTM D1525, ISO 306/A 6 5 |
| -- | 236 | °C | ASTM D1525, ISO 306/B 7 6 |
| Melting Temperature | 250 to 256 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.550 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| 3.20 mm | V-0 | ||
| Glow Wire Flammability Index (1.20 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.20 mm) | 775 | °C | IEC 60695-2-13 |
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 90.0 | °C | |
| Pre-heater | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 6x4x50 mm |
| 3 . | 20000 hrs |
| 4 . | Heat Stabilized, 20000 hrs |
| 5 . | Loading 1 (10 N) |
| 6 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenac™ 4012 | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| LUVOCOM® 1104-8928 | Lehmann & Voss & Co. | PEK | LUVOCOM® |
| Sylvin 5170-85 White 1539 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Elvax® CE9619-1 | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Durethan® BM 25 FN20 DUS013 000000 | LANXESS GmbH | Nylon 6 | Durethan® |