Hanwha Total PP BI730
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PKnCVH_Hanwha-Total-PP-BI730.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BI730 is a highly isotactic block copolymer with high flowability, high strength, and high crystalinity. It shows an excellent balance of strength and impact resistance due to the application of high crystalline technology and the most appropriate rubber design. BI730 also has a broad molecular weight distribution so that it has better injection processibility compared to general PP. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 91 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 29.4 | MPa | ASTM D638 |
| Flexural Modulus | 1570 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 39 | J/m | ASTM D256 |
| 23°C | 78 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 127 | °C | ASTM D648 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss | 75 | ASTM D2457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 160 - 200 | °C | |
| Middle Temperature | 200 - 240 | °C | |
| Front Temperature | 220 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Pressure | 98.1 - 245 | MPa | |
| Holding Pressure | 78.5 - 226 | MPa |
| Injection instructions |
|---|
| Cooling Time: 25 to 40 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycal™ 1820T3 Bk-1 | Technical Polymers, LLC | Nylon 6 | Nycal™ |
| Lucet® N127-02 | LG Chem Ltd. | Acetal (POM) Copolymer | Lucet® |
| Lupoy® SG5009F | LG Chem Ltd. | PC+ABS | Lupoy® |
| Pinnacle PP 2150H | Pinnacle Polymers | PP Impact Copolymer | Pinnacle PP |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |