| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ZPbFVF_MAJORIS-BT231---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BT231 - 8229 is a 20% mineral filled grade intended for injection moulding and blow moulding. The product is available in natural (BT231) and black (BT231 - 8229) but other colours can be supplied on request. BT231 - 8229 has been developed especially for the automotive under hood applications requiring very good long-term heat stability. APPLICATIONS Products requiring high rigidity, very good long- term heat resistance, high heat distortion temperature, low shrinkage and high dimensional stability such as:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.1 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 77 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2600 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 38.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 53 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 6.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 127 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 70.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 156 | °C | ISO 306/A |
| -- | 105 | °C | ISO 306/B |
| Melting Temperature (DSC) | 163 | °C | ISO 3146 |
| Thermal Stability (150°C) | > 700.0 | hr |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Atomization- 100°C/16H | 2.0E-4 | g | DIN 75201 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 - 250 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 - 230 | °C | |
| Cylinder Zone 3 Temp. | 190 - 230 | °C | |
| Cylinder Zone 5 Temp. | 190 - 230 | °C | |
| Melt Temperature | 180 - 230 | °C | |
| Die Temperature | 180 - 230 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V738 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Small Boss SPVC2005 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Flexible | Small Boss |
| Veroplas K160 | PlastxWorld Inc. | Acrylic (PMMA) | Veroplas |
| ALTECH® NXT PP-B A 2035/450 GF35 CP | ALBIS PLASTIC GmbH | PP Copolymer | ALTECH® NXT PP-B |
| CERTENE™ HPB-0354 | Muehlstein | HDPE | CERTENE™ |