Tecodur® PB70 CR30 BK111
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecodur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PDr825_Tecodur-PB70-CR30-BK111.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT, 30% carbon fiber reinforced, black |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 0.080 | % | ISO 15512 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 24000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.5 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 6.0 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 40 | kJ/m² | |
| 23°C | 45 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature 1 | 225 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | < 1.0E+3 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.60 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Hopper Temperature | 50.0 to 70.0 | °C | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 40.0 to 80.0 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF J-2 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| Sultron® 70C6 | Asia International Enterprise (Hong Kong) Limited | PPS | Sultron® |
| Vyncolit® X7500 | Vyncolit N.V. | Phenolic | Vyncolit® |
| MAJORIS FFRH260R | AD majoris | PP, Unspecified | MAJORIS |
| Polifor® 8 GB/20 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |