CONTINUUM™ DMDE-6620 NT 7 HEALTH+™ BIMODAL
| Category: | HDPE , Bimodal Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | CONTINUUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | XOF4Nz_CONTINUUMDMDE6620NT7HEALTHBIMODAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
CONTINUUM™ DMDE-6620 NT 7 HEALTH+™ Bimodal High Density Polyethylene Resin is produced by UNIPOL™ II process technology. This resin is a high stiffness resin with superior top-load performance in conjunction with excellent environmental stress crack resistance and excellent gas barrier properties. CONTINUUM™ DMDE-6620 NT 7 HEALTH+™ Bimodal is specifically designed for use in multiple types of blow molding processes, producing containers up to 20 gallons in size, which require superior top-load combined with excellent environmental stress crack resistance and gas barrier properties. This product offers excellent processability with low plate out properties. This product is especially well suited for containers used to package health care and pharmaceutical products.
Complies with:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.28 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 27 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 10% Igepal, F50 | 220 | hr | ASTM D1693 |
| 50°C, 100% Igepal, F50 | > 1100 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 59 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 28.0 | MPa | ASTM D638 |
| Fracture | 18.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 8.0 | % | ASTM D638 |
| Fracture | 670 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1170 | MPa | ASTM D790B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 82.0 | °C | ASTM D648 |
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 131 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 133 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 121 | °C | Internal method |
| Additional Information |
|---|
| Plaque molded and tested in accordance with ASTM D4976. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starflam AFR470X2 | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Sypex S1420GN | Ginar Technology Co., LTD. | SAN | Sypex |
| Tarnamid® T- 27 M | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| Bergamid™ A700 G25 U-S01 NC041 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| ESTOPLAST EP 2030GY39 | Ester Industries Ltd. | PBT | ESTOPLAST EP |