LNP™ STAT-KON™ QE002S compound
| Category: | Nylon 610 , Polyamide 610 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ObNP0l_LNP-STAT-KON-QE002S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON QE002S is a compound based on Nylon 6/10 containing 10% carbon Fiber. Added features of this material include: Heat Stabilized, Electrically Conductive. Also known as: LNP* STAT-KON* Compound QC-1002 HS Product reorder name: QE002S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.40 to 0.60 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.28 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.37 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8480 | MPa | ASTM D638 |
| -- | 8380 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 144 | MPa | ASTM D638 |
| Break 3 | 143 | MPa | ASTM D638 |
| Break | 142 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 2.8 | % | ASTM D638 |
| Break 5 | 2.9 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 7160 | MPa | ASTM D790 |
| -- 7 | 6720 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 195 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 201 | MPa | ASTM D790 |
| Break, 50.0 mm Span 9 | 197 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 10 | 4.4 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 480 | J/m | ASTM D4812 |
| 23°C 11 | 32 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 7.32 | J | ASTM D3763 |
| -- | 1.24 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 222 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 12 | 220 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 205 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 13 | 203 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.8E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 8.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+4 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 1.3 mm/min |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP EMI 2163 | RTP Company | PEI | RTP |
| Sindustris PP GP3401S | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Yuyao PP TL203 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| NEFTEKHIM PP 3840K (T2101F) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| HiFill® PP GB50 | Techmer Engineered Solutions | PP, Unspecified | HiFill® |