Ferro PP MPP20FJ11NA
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ferro Corporation |
| Trademark: | Ferro PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 746Hsv_Ferro-PP-MPP20FJ11NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ferro PP MPP20FJ11NA is a Polypropylene Homopolymer (PP Homopolymer) material filled with 21% mica. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Ferro PP MPP20FJ11NA: Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 27 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.4 | % | |
| Across Flow | 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 29.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 8.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant : 23°C | 2050 | MPa | |
| Tangent : 23°C | 2520 | MPa | |
| Flexural Strength (23°C) | 44.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 27 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 340 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 0.565 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 121 | °C | |
| 1.8 MPa, Unannealed | 65.6 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Rear Temperature | 204 to 213 | °C | |
| Middle Temperature | 210 to 216 | °C | |
| Front Temperature | 216 to 218 | °C | |
| Nozzle Temperature | 218 to 227 | °C | |
| Mold Temperature | 43.3 to 57.2 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Polyethylene F320 | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Crastin® HR5315HF NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Elastollan® LP 9307 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| POLYfill PP CIQ10015ER UV | Polykemi AB | PP, Unspecified | POLYfill |
| LEXAN™ HFD1014 resin | SABIC Innovative Plastics | PC | LEXAN™ |