| Polycarbonate, Low Flow |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ISO 294-4 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 120 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 120 | % | ISO 527-2 |
| Flexural Modulus | 1970 | MPa | ISO 178 |
| Flexural Stress | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 67 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 148 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 138 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® VKM 24 NERO900 | SO.F.TER. SPA | PP Homopolymer | Tecnoprene® |
| Tecomid® NA40 GR13 NL100 MB | Eurotec Engineering Plastics | Nylon 66 | Tecomid® |
| DIC.PPS EC-40B | DIC Corporation | PPS | DIC.PPS |
| Hostacom HBG H01 BLACK | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LNP™ THERMOCOMP™ WC006 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |