Arak LLDPE LL1209AA / LL1209KJ

Category:	LLDPE , Linear Low Density Polyethylene
Manufacturer:	Shazand (Arak) Petrochemical Corporation
Trademark:	Arak LLDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MQ1WMK_Arak-LLDPE-LL1209AA-LL1209KJ.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
LL1209AA & LL1209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer. LL1209AA & LL1209KJ are suitable for co extrusion blown films with the following advantages: Improved hot-tack. Good optical properties. Low gel level and low odour. Good substrate adhesion. Tough core layer. Typical applications for LL1209AA & LL1209KJ are lamination films and heat sealing layers. Also LL1209KJ is highly recommended for display packaging. LL1209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance. Recommended melt temperature for extrusion is about 180°C-225°C. LL1209AA & LL1209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight. * LL1209AA & LL1209KJ are suitable for food contact.

Message

LL1209AA & LL1209KJ are linear low density polyethylene copolymers containing butene-1 as a co-monomer. LL1209AA & LL1209KJ are suitable for co extrusion blown films with the following advantages:

Improved hot-tack.

Good optical properties.

Low gel level and low odour.

Good substrate adhesion.

Tough core layer.

Typical applications for LL1209AA & LL1209KJ are lamination films and heat sealing layers. Also LL1209KJ is highly recommended for display packaging.

LL1209KJ offers high slip film with easy opening properties when used pure in thickness range 35-100 microns. Addition of other polymers, master batches and pigments or use of other thickness may alter film slip and anti-block performance.

Recommended melt temperature for extrusion is about 180°C-225°C.

LL1209AA & LL1209KJ should be stored in the dry condition below the 50°C and avoided from the exposure of direct sunlight.

* LL1209AA & LL1209KJ are suitable for food contact.

General Information
Additive	High Slip
Features	Butene Comonomer Copolymer Food Contact Acceptable Good Adhesion Good Heat Seal Good Toughness High Slip Hot Tack Strength Low Gloss Low to No Odor Opticals
Uses	Cable Jacketing Film Laminates Packaging
Processing Method	Blown Film

Physical	Nominal Value	Unit	Test Method
Density	0.920	g/cm³	ASTM D2838
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	0.90	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	38	µm
Film Thickness - Recommended / Available	35 to 100µm
Tensile Strength			ASTM D882
MD : Yield	9.50	MPa
TD : Yield	9.50	MPa
MD : Break	38.0	MPa
TD : Break	28.0	MPa
Tensile Elongation			ASTM D882
MD : Break	450	%
TD : Break	800	%
Dart Drop Impact	150	g	ASTM D1709
Elmendorf Tear Strength			ASTM D1922
MD : 25 µm	85	g
TD : 25 µm	530	g

Optical	Nominal Value	Unit	Test Method
Gloss (45°)	70		ASTM D2457
Haze	5.0	%	ASTM D1003

Extrusion	Nominal Value	Unit
Melt Temperature	180 to 225	°C

Resin Grade	Manufacturer	Category	Trademark
Gebablend 65	geba Kunststoffcompounds GmbH	PC+ABS	Gebablend
KumhoSunny PBT 3710G	Shanghai KumhoSunny Plastics Co., Ltd.	PBT	KumhoSunny PBT
Lion Idemitsu Composites PPS C-600SG	Lion Idemitsu Composites Co., Ltd.	PPS	Lion Idemitsu Composites PPS
Karina CLEAR ( CRYSTAL ) PVC COMP -E 85/201-IS	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
Sumikon® FM-TC122	SBHPP	PC	Sumikon®