Lustran® ABS 451
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | MPVfrZ_Lustran-ABS-451.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Lustran ABS 451 is a soft flowing, medium impact injection molding resin designed with a unique balance of impact, heat resistance, flow and gloss. As with any product, use of Lustran ABS 451 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 4.4 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 107 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2620 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 42.7 | MPa | ASTM D638 |
| Flexural Modulus | 2590 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 74.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -18°C, 3.18 mm | 69 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 180 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 12.7mm | 80.6 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 102 | °C | ASTM D648 |
| Vicat Softening Temperature | 96.1 | °C | ASTM D1525 1 |
| CLTE - Flow | 8.3E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.2 - 87.8 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Shot Size | 50 - 75 | % | |
| Processing (Melt) Temp | 232 - 274 | °C | |
| Mold Temperature | 43.3 - 65.6 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Cushion | < 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 | ||
| Vent Depth | 0.051 | mm |
| Injection instructions |
|---|
| Screw Speed: ModerateScrew Delay: to minimize residence |
| Note Message | |
|---|---|
| 1 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209 K FR | RTP Company | PARA | RTP |
| MOSTEN MA 612 | UNIPETROL RPA | PP Impact Copolymer | MOSTEN |
| ALTECH® ABS A 2015/506 GF15 | ALBIS PLASTIC GmbH | ABS | ALTECH® ABS |
| ECONAMID® 6FL | DOMO Engineering Plastics SPA | Nylon 6 | ECONAMID® |
| POLYFORT® FPP 20 TE | A. Schulman Europe | PP Homopolymer | POLYFORT® |