Mafill® HF 4002
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Ravago Group |
| Trademark: | Mafill® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSAKu4_Mafill-HF-4002.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PP Homo V2 Deca-BDE free |
| General Information | |
|---|---|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.5 to 1.8 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 28.0 | MPa | |
| Break | 18.0 | MPa | |
| Tensile Strain (Break) | 50 | % | ISO 527-2 |
| Flexural Modulus | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 90.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | ||
| 3.20 mm | V-2 | ||
| Glow Wire Flammability Index (2.00 mm) | 850 | °C | IEC 60695-2-12 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 8742 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| EPO-TEK® H70E-2 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| K-vinyl 105 Deg C Rating Insulation (90-Wet) | Technovinyl Polymers India Ltd. | PVC, Unspecified | K-vinyl |
| Petlon R-Prime PET Clear 100 FR-36 | Petlon Polymers Ltd | PET | Petlon R-Prime |
| Plasmer 1380N/1002 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |