Bayflex® 963

Category:	PUR-MDI , Polyurethane (MDI)
Manufacturer:	Covestro - PUR
Trademark:	Bayflex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	MCGW4I_Bayflex-963.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Bayflex 963 is a fully compounded polyether-based polyurethane system consisting of two liquid components which can be water-blown. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. The Bayflex 963 system is used in the manufacture of microcellular polyurethane innersoles. The innersoles prepared from these compounds combine light weight, comfort, and durability. Processibility and dynamic flexural properties are excellent and have made the Bayflex 963 system a prime innersole material. As with any product, use of the Bayflex 963 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. The properties of the Bayflex 963 system, listed below, are representative of typical performance characteristics of molded panels. Actual results may vary, depending on part design and processing conditions.

General Information
Features	Workability, good Good flexibility
Uses	Footwear

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.304	g/cm³	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness	60		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Strength (Break)	2.07	MPa	ASTM D412
Tensile Elongation (Break)	500	%	ASTM D412
Tear Strength ¹	1.40	kN/m	Internal method
Compression Load Deflection at 25%	0.0517	MPa	ASTM D575
Compression Load Deflection at 50%	0.138	MPa	ASTM D575
Compression Set (25°C, 22 hr)	4.0	%	ASTM D395

Thermoset	Nominal Value
Thermoset Components
Component a	Mixing ratio by weight: 69
Component B	Mixing ratio by weight: 100

Additional Information
Part A Type: Isocyanate Appearance: Light yellow viscous liquid Specific Gravity @ 25°C: 1.20 Viscosity @25°C: 1100 mPas Flash Point PMCC: 207°C Bulk Density @ 20°C:10.01 lb/gal NCO: 18.7 - 19.1 wt% Part B Type: Polyol Appearance: Milky white liquid Specific Gravity @ 25°C: 1.06 Viscosity @25°C: 1100 mPas Flash Point PMCC: 126°C Bulk Density @ 25°C: 8.85 lb/gal Water: 0.83 wt% Hydroxyl Number: 125 Material Temperature: 25 to 30°CMold Temperature: 43 to 49°CDemold Time: 3.5 minLinear Shrinkage@ 0.5 g/cm: <1.0%Hand Mix Reactivity @ 25°C Cream Time: 10 to 15 sec Tack Free: 45 to 55 sec Pull Time: 55 to 65 sec Free-Rise Density: 8 to 11 lb/ft³

Additional Information

Part A Type: Isocyanate Appearance: Light yellow viscous liquid Specific Gravity @ 25°C: 1.20 Viscosity @25°C: 1100 mPa*s Flash Point PMCC: 207°C Bulk Density @ 20°C:10.01 lb/gal NCO: 18.7 - 19.1 wt% Part B Type: Polyol Appearance: Milky white liquid Specific Gravity @ 25°C: 1.06 Viscosity @25°C: 1100 mPa*s Flash Point PMCC: 126°C Bulk Density @ 25°C: 8.85 lb/gal Water: 0.83 wt% Hydroxyl Number: 125 Material Temperature: 25 to 30°CMold Temperature: 43 to 49°CDemold Time: 3.5 minLinear Shrinkage@ 0.5 g/cm: <1.0%Hand Mix Reactivity @ 25°C Cream Time: 10 to 15 sec Tack Free: 45 to 55 sec Pull Time: 55 to 65 sec Free-Rise Density: 8 to 11 lb/ft³

Note Message
1 .	Block

Resin Grade	Manufacturer	Category	Trademark
WELLAMID Nylon 6000 GV 25 HWCP	CP-Polymer-Technik GmbH & Co. KG	Nylon 6	WELLAMID Nylon
Fainplast PVC PK 8025	Fainplast Compounds S.r.l	PVC, Flexible	Fainplast PVC
FRIANYL® C3 H V0	Nilit Plastics	Nylon 66/6	FRIANYL®
HIPLEX® HHM 5502	HIP-PetroHemija	HDPE	HIPLEX®
Sylvin 3230-80 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin