RTP 103 CC
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iTlLKB_RTP-103-CC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - Chemically Coupled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Moisture Content | < 0.20 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Primary Additive | 20 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ASTM D638 |
| Tensile Strength | 60.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 3520 | MPa | ASTM D790 |
| Flexural Strength | 90.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 93 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 560 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 152 | °C | |
| 1.8 MPa, Unannealed | 129 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RMA 65 | Ronald Mark Associates, Inc. | PVC Homopolymer | RMA |
| Trademark PP PPR5500MA | Trademark Plastics Corporation | PP Random Copolymer | Trademark PP |
| Nipol® NBR N30L | Zeon Corporation | NBR | Nipol® NBR |
| HiFill® PA6 GF25 L BK | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Huafon HF-4095A | Huafon Group Co., Ltd. | TPU-Polyether | Huafon |