Baytec® MS-092 (BDO)
| Category: | PUR-Ester/MDI , Polyurethane (Polyester, MDI) |
| Manufacturer: | Covestro - PUR |
| Trademark: | Baytec® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | LthdRy_Baytec-MS-092-BDO-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Baytec MS-092 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer. It is used in the manufacture of high-property solid cast polyurethane elastomers. As with any product, use of Baytec MS-092 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Forms |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shaw A | 93 | ASTM D2240 | |
| Shaw D | 43 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (1000 Cycles, 1000 g, H-18 Wheel) | 30.0 | mg | ASTM D3498 |
| Compression Deflection | ASTM D575 | ||
| 10% | 3.65 | MPa | ASTM D575 |
| 15% | 5.17 | MPa | ASTM D575 |
| 2% | 0.517 | MPa | ASTM D575 |
| 20% | 6.69 | MPa | ASTM D575 |
| 25% | 8.27 | MPa | ASTM D575 |
| 5% | 1.90 | MPa | ASTM D575 |
| 50% | 22.9 | MPa | ASTM D575 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 10.2 | MPa | ASTM D412 |
| 200% strain | 13.5 | MPa | ASTM D412 |
| 300% strain | 17.9 | MPa | ASTM D412 |
| Tensile Strength (Break) | 47.4 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 510 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 118 | kN/m | ASTM D624 |
| Cracking | 48 | kN/m | ASTM D1938 |
| Compression Set (70°C, 22 hr) | 22 | % | ASTM D395 |
| Bayshore Resilience | 43 | % | ASTM D2632 |
| Additional Information |
|---|
| Appearance: Pale yellow liquidNCO: 8.95 to 9.34 wt%Flash Point, PMCC: 222°CSpecific Gravity at 80°C: 1.15Specific Gravity at 100°C: 1.13Viscosity at 80°C: 750 mPa-sViscosity at 100°C: 365 mPa-sNCO/OH Ratio: 1.05Stoichiometry: 95% TheoryPrepolymer Temperature: 80 to 95°CExtender Temperature: 25 to 70°CMold Temperature: 100 to 110°CPot Life: 2 to 6 minDemold: 30 min |
| Note Message | |
|---|---|
| 1 . | C mould |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7105D | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Sumitomo Phenolic FM 1132P | Sumitomo Bakelite North America, Inc. | Phenolic | Sumitomo Phenolic |
| VITAMIDE® BG35BK6357 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Flexalloy® OR 9800-50 | Teknor Apex Company | PVC Elastomer | Flexalloy® |
| EnCom F2 PC 1212 | EnCom, Inc. | PC | EnCom |