LNP™ LUBRICOMP™ IFL36 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | KzaDwG_LNPLUBRICOMPIFL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP IFL36 is a compound based on PA6.12 resin, containing Glass Fiber and PTFE. Added features include: internally lubricated. Also known as: LNP* LUBRICOMP* Compound IFL-4036 Product reorder name: IFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 117 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 7200 | MPa | ISO 178 |
| Flexural Stress | 166 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.46 | ASTM D3702 Modified | |
| With Self-Static | 0.48 | ASTM D3702 Modified | |
| Wear Factor - Washer | 14.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 45 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 212 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 194 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.4E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 1.3E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 - 0.20 | % | |
| Rear Temperature | 254 - 266 | °C | |
| Middle Temperature | 260 - 271 | °C | |
| Front Temperature | 271 - 282 | °C | |
| Processing (Melt) Temp | 271 - 277 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 7860 | TOTAL Refining & Chemicals | PP Copolymer | TOTAL Polypropylene |
| Vydyne® 21SPF BLK | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| NEXUS PP CPP8/2 | Nexus Resin Group, LLC. | PP Impact Copolymer | NEXUS PP |
| 4PROP® 9C11120 XHFR1 | 4Plas | PP Copolymer | 4PROP® |
| KOCETAL® GB705 | Kolon Plastics, Inc. | Acetal (POM) Copolymer | KOCETAL® |